Company | Alloys | Services | Products | Ordering | Contact
Profile Capabilities News Site map
Rolling Bar forging Press forging Forgeable alloys
Waterjet Cutting
Request quote All Alloys - high temperature HASTELLOY alloy X (HX) INCONEL alloy 625 INCONEL alloy 718 INCONEL alloy 601 HAYNES alloy 25 (L605) NITRONIC 60 - corrosion resistant HASTELLOY alloy C-276 MONEL alloy K-500 INCONEL alloy 625 INCOLOY alloy 25-6HN FERRALIUM alloy 255 NITRONIC 60 NITRONIC 50 HAYNES alloy 25 NITRONIC 30 - wear resistant HPA COBALT alloy 6B HPA COBALT alloy 6BH NITRONIC 60 NITRONIC 30
Product Catalog Quick Reference Bar Wire Sheet Plate Fasteners Forgings Corrosion resistant Wear resistant High temperature
Request quote Bar Inventory Plate Inventory Payment
Contact info Request quote Request info Order survey form Quote survey form

Alloys

 
  ^up all alloys corrosion resistant wear resistant high temperature forgeable  
 

INCOLOY® alloy 800H (UNS N08811) Ni 32.5 Cr 21 Mn 1.5 C 0.10 Si 1.0 Fe 39.5 Cu 0.75 S 0.015 Al 0.60 max. Ti 0.60 max

High Performance Alloys stocks and produces this grade in the following forms: Bar, sheet, plate, fasteners and forgings. Request quote on this grade.

 

Overview

UNS N08810 / UNS N08811
800HT is an iron-nickel-chromium alloy having the same basic composition as Alloy 800, with significantly higher creep rupture strength. The higher strength results from close control of carbon, aluminum and titanium contents in conjunction with a high temp anneal. The 800H modification was to control carbon (0.05 to 0.10%) and grain size to (>ASTM 5) to optimize stress rupture properties. 800HT has further modifications to the combined titanium and aluminum levels (0.85 to 1.2%) to ensure optimum high temperature properties. The alloy is dual certified and combines the properties of both forms.

The chemical balance allows the alloy to exhibit excellent resistance to carburization, oxidation and nitriding atmospheres. 800HT will not become embrittled even after long periods of usage in the 1200-1600 deg F range where many stainless steels become brittle. Excellent cold forming characteristics typically associated with the nickel-chromium alloys are exhibited with 800HT. When cold formed extensively the grain size produces a visibly undulated surface called "orange peel". 800HT can be welded by the common techniques used on stainless steels.

Typical applications for the alloy include ethylene pyrolysis, hydrocarbon cracking, cracking furnaces for vinyl chloride, diphenol and acetic acid. The alloy is also used for valves, fittings and other components exposed to corrosive attack from 1100 to 1800 deg F.

Round bar ranging from 3/4" to 6" diameter, and light gauge sheet and plate. Material can be supplied in random lengths, cut to order or machined to customer requirements. Machining includes drilling, threading, milling, CNC shapes, turning, tapping, flanges and others.

Chemistry

Chemical Requirements

Ni

Cr

Mn

C

Si

Fe

C

Max

35.0

23.0

1.5

0.10

1.0

0.75

Min

30.0

19.0

39.5

Tensile Data

Mechanical Property Requirements

Ultimate Tensile, min.

Yield Strength (0.2% OS)

Elong. in 2 in. or 50mm (or 4D) min., %

R/A

Hardness

Min

80 KSi

35 KSi

25

Max

Min

550 MPa

240 MPa

Max

 

Mechanical Property Requirements

Ultimate Tensile, min.

Yield Strength (0.2% OS)

Elong. in 2 in. or 50mm (or 4D), min.,%

R/A

Hardness

Cold Worked/Annealed

Min

75 KSI

30 KSi

30

Max

Min

515 MPa

205 Mpa

Max

Hot Worked/Annealed

Min

75 KSi

30 KSi

30

Max

Min

515 Mpa

205 MPa

Max

Specifications

Form

Standard

Metal Type

UNS N08800 / N08810 / N08811

Bar

ASTM B408

Wire

Sheet

ASTM B409

Plate

ASTM B409

Fitting

ASTM B366

Forging

ASTM B564

Weld Wire

 

Weld Electrode

 

Machining

MACHINING DATA
Carbide tools are suggested
for rates better than 50% of Type 304.
Machining Type Suggested starting rates are:
Single Point turning : Roughing - 0.15" depth, 0.015"/rev feed -175 SFM
Finishing - 0.025" depth, 0.007"/rev feed - 200 SFM
Drilling : 1/4" Dia hole - 0.004"/rev feed - 60 SFM
1/2" Dia hole - 0.007"/rev feed - 60 SFM
3/4" Dia hole - 0.010"/rev feed - 60 SFM
Reaming : Feed - same as drilling - 100 SFM
Side and Slot Milling : Roughing - 0.25" depth - 0.007"/tooth feed - 125SFM
Finishing - 0.050" depth - 0.009"/tooth feed - 140SFM
These rates are for carbide tools,
Type C-2 for roughing, drilling and reaming.
Type C-3 for finishing.

 


INCOLOY® is a registered trademark of the INCO family of companies.

 
 
   
 
©2007 High Performance Alloys, Inc. Reproduction of this site in whole or part is prohibited without the expressed permission of High Performance Alloys.
ISO 9001:2008 Registered Manufacturer & Distributor. Please read our product Disclaimer and Terms & Conditions
Share |